產(chǎn)品簡介：分散在甲苯溶液中油溶性的InP-ZnS核殼熒光量子點，表面功能化活性基團為NH2-Amine functional ligands氨基。

Product name: InP-ZnS Core/Shell Quantum Dot in Toluene

Emisson tolerance: ±10 nm

FWHM（半峰寬）: 25-35 nm

Quantum yield(量子產(chǎn)率):  50%-90%

Surface group: Amine(NH2)

Concentreation：5mg/ml

Solvent: Toluene

Storage: 4-25℃ in the dark, Do not freeze ,12 months

500 nm InP-ZnS Fluorescent nanocrystals coated with amine surface ligand, in Toluene

520 nm InP-ZnS Fluorescent nanocrystals coated with amine surface ligand, in Toluene

540 nm InP-ZnS Fluorescent nanocrystals coated with amine surface ligand, in Toluene

560 nm InP-ZnS Fluorescent nanocrystals coated with amine surface ligand, in Toluene

580 nm InP-ZnS Fluorescent nanocrystals coated with amine surface ligand, in Toluene

600 nm InP-ZnS Fluorescent nanocrystals coated with amine surface ligand, in Toluene

620 nm InP-ZnS Fluorescent nanocrystals coated with amine surface ligand, in Toluene

640 nm InP-ZnS Fluorescent nanocrystals coated with amine surface ligand, in Toluene

摘要：

   采用溶膠-凝膠法,通過調(diào)整實驗參數(shù)和工藝條件,制備得到尺寸分散均勻、具有強綠光發(fā)射的ZnO量子點。通過紫外-可見吸收光譜和瞬態(tài)光譜結(jié)果分析,可得出ZnO量子點的吸收為本征吸收,綠光發(fā)射為與氧空位有關(guān)的缺陷發(fā)光。 在制備得到分散均勻ZnO量子點的基礎(chǔ)上,本實驗利用帶有不同官能團的有機表面修飾劑,如油酸、聚乙烯吡咯烷酮、十二胺、十二硫醇和巰基乙酸對ZnO量子點進行表面修飾。通過透射電鏡結(jié)果觀察,可得到分散均勻的納米ZnO。同時,通過紅外譜圖和XPS光電子譜圖表征,證明這些有機表面修飾劑修飾在ZnO量子點的表面。 對修飾后ZnO量子點的發(fā)光性能進行了表征,通過分析光致發(fā)光譜、紫外-可見吸收光譜和瞬態(tài)光譜結(jié)果,對比了修飾前后ZnO量子點的發(fā)光性能。研究發(fā)現(xiàn)經(jīng)表面修飾劑修飾后,ZnO量子點的發(fā)光強度或發(fā)光峰位發(fā)生了改變。同時,ZnO量子點的綠光發(fā)射的熒光壽命均發(fā)生縮短,這進一步驗證了修飾劑的作用,說明量子點的表面態(tài)發(fā)生改變,導致量子點發(fā)光路徑的改變,使其熒光壽命縮短。